Laves-phase evolution during aging in 9Cr-1.8W-0.5Mo-VNb steel for USC power plants

Wang, Xue, Xu, Qiang, Yu, Shu-min, Hu, Lei, Liu, Hong and Ren, Yao-yao (2015) Laves-phase evolution during aging in 9Cr-1.8W-0.5Mo-VNb steel for USC power plants. Materials Chemistry and Physics, 163. pp. 219-228. ISSN 0254-0584

[img]
Preview
PDF - Accepted Version
Download (2MB) | Preview

Abstract

Long term precipitation and coarsening of Laves-phase in tungsten strengthened 9% Cr steel under thermal aging at 923 K was investigated and reported in this paper. It experimentally measured the evolution of mean particle size, the number density, the volume fraction of Laves-phase precipitates, the partition coefficients of W and Mo in the matrix, as well as the change of hardness. Its main conclusions were: 1) Laves-phase nucleates and grows rapidly on grain boundaries and lath boundaries within the first 1500 h of aging time; 2) The two stages characteristics and kinetics of Laves-phase nucleation and growth which were determined experimentally; 3) The coarsening of Laves-phase is much faster than that of M23C6 carbides; 4) The precipitation of Laves-phase produces a pronounced matrix depletion of W and Mo atoms; and 5) The precipitated Laves-phase gives rise to weaker precipitation strengthening in comparison with M23C6 carbides, and causes the loss of hardness due to the depletion of Mo and W from the solid solution. This paper contributes to the knowledge of kinetics of Laves-phase precipitation and coarsening, providing the essential information for comparative investigation of creep damage mechanisms. This paper also contributes to the understanding the creep damage broadly.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Schools: School of Computing and Engineering
Related URLs:
Depositing User: Cherry Edmunds
Date Deposited: 16 Sep 2015 10:55
Last Modified: 05 Dec 2016 02:50
URI: http://eprints.hud.ac.uk/id/eprint/25730

Downloads

Downloads per month over past year

Repository Staff Only: item control page

View Item View Item

University of Huddersfield, Queensgate, Huddersfield, HD1 3DH Copyright and Disclaimer All rights reserved ©