Smith, Alan M., Harris, Jonathan J., Shelton, Richard M. and Perrie, Yvonne (2007) 3D culture of bone-derived cells immobilised in alginate following light-triggered gelation. Journal of Controlled Release, 119 (1). pp. 94-101. ISSN 0168-3659
Abstract

Photoreactive liposomes have been exploited as a means of developing 3D tissue constructs. Liposomes formulated using the photosensitive lipid 1,2-bis(4-(n-butyl)phenylazo-4′phenylbutyroyl)phosphatidylcholine (Bis Azo PC), which undergoes conformational change on stimulation with long wavelength ultraviolet light, were prepared with entrapped CaCl2 before being incorporated into a 4% alginate solution. It was shown that stimulation of the photosensitive lipid using a light emitting diode (LED) (peak emission at 385 nm, dose equivalent to 9 mJ/cm2) caused the release of liposome entrapped CaCl2, resulting in cross-linking of the alginate solution and immobilisation of bone derived cells over a range of seeding densities, approximately 97% of which remained viable for periods of up to 14 days in culture. Entrapment volumes of a variety of liposome types were evaluated and interdigitating fusion vesicles were identified as having the highest payload (24%), however the inclusion of cholesterol as a means of shifting Bis Azo PC sensitivity into the visible light wavelengths resulted in an approximately 10-fold reduction in calcium entrapment. This application of light-sensitised liposomes offers the potential to create complex tissue engineering substrates containing cells immobilised in precise locations, in contrast with substrates onto which cells are seeded post production.

Information
Library
Documents
[thumbnail of JCR_Liposomes_alginate.pdf]
JCR_Liposomes_alginate.pdf
Restricted to Repository staff only

Download (709kB)
Statistics
Add to AnyAdd to TwitterAdd to FacebookAdd to LinkedinAdd to PinterestAdd to Email