Reproduction of fretting wear at the stem—cement interface in total hip replacement

Brown, Leigh, Zhang, H., Blunt, Liam and Barrans, Simon (2007) Reproduction of fretting wear at the stem—cement interface in total hip replacement. Proceedings of the Institution of Mechanical Engineers, Part H: Journal of Engineering in Medicine, 221 (8). pp. 963-971. ISSN 0954-4119

[img]
Preview
PDF
Download (578kB) | Preview

    Abstract

    The stem-cement interface experiences fretting wear in vivo due to low-amplitude oscillatory micromotion under physiological loading, as a consequence it is considered to play an important part in the overall wear of cemented total hip replacement. Despite its potential significance, in-vitro simulation to reproduce fretting wear has seldom been attempted and even then with only limited success. In the present study, fretting wear was successfully reproduced at the stem-cement interface through an in-vitro wear simulation, which was performed in part with reference to ISO 7206-4: 2002. The wear locations compared well with the results of retrieval studies. There was no evidence of bone cement transfer films on the stem surface and no fatigue cracks in the cement mantle. The cement surface was severely damaged in those areas in contact with the fretting zones on the stem surface, with retention of cement debris in the micropores. Furthermore, it was suggested that these micropores contributed to initiation and propagation of fretting wear. This study gave scope for further comparative study of the influence of stem geometry, stem surface finish, and bone cement brand on generation of fretting wear.

    ▼ Jump to Download Statistics
    Item Type: Article
    Additional Information: Published in the Proceedings of the Institution of Mechanical Engineers, Part H: Journal of Engineering in Medicine, 221(8),2007. Copyright ©2007 Professional Engineering Publishing.
    Subjects: T Technology > T Technology (General)
    T Technology > TA Engineering (General). Civil engineering (General)
    Schools: School of Computing and Engineering
    School of Computing and Engineering > Centre for Precision Technologies
    School of Computing and Engineering > Centre for Precision Technologies > Engineering Control and Machine Performance Research Group
    School of Computing and Engineering > Centre for Precision Technologies > Surface Metrology Group
    School of Computing and Engineering > Pedagogical Research Group
    School of Computing and Engineering > Turbo Research Institute
    Related URLs:
    References:

    Mjoberg, B. The theory of early loosening of hip prostheses. Orthopedics, 1997, 20, 1169-1175.

    Herberts, P. and Malchau, H. Long term registration has improved the quality of hip replacement: a review of the Swedish THR Register comparing 160,000 cases. Acta Orthop. Scand., 2000, 71, 111-121. [CrossRef]

    Rubash, H. E., Sinha, R. K., Shanbhag, A. S. and Kim, S. Y. Pathogenesis of bone loss after total hip arthroplasty. Orthop. Clinics North Am., 1998, 29, 173-186. [CrossRef]

    Ingham, E. and Fisher, J. Biological reactions to wear debris in total joint replacement. Proc. Instn Mech. Engrs, Part H: J. Engineering in Medicine, 2000, 214(H1), 21-37.

    Verdonschot, N. and Huiskes, R. Cement debonding process of total hip arthroplasty stems. Clin. Orthop. Relat. Res., 1997, 336, 297-307.

    Mohler, C. G., Callaghan, J. J., Collis, D. K. and Johnston, R. C. Early loosening of the femoral component at the cement-prosthesis interface after total hip replacement. J. Bone Jt Surg. Br., 1996, 78, 280-285.

    Kiss, J., Murray, D. W., Turner-Smith, A. R., Bithell, J. and Bulstrode, C. J. Migration of cemented femoral components after THR. J. Bone Jt Surg. Br., 1996, 78, 796-801.

    Karrholm, J., Nivbrant, B., Thanner, J., Anderberg, C., Börlin, N., Herberts, P. and Malchau, H. Radiostereometric evaluation of hip implant design and surface finish: micromotion of cemented femoral stems. 67th Annual Meeting of the American Academy of Orthopaedic Surgeons, Orlando, Florida, USA, 15-19 March 2000.

    Wroblewski, B. M., Siney, P. D., Dowson, D. and Collins, S. N. Prospective clinical and joint simulator studies of a new total hip arthroplasty using alumina ceramic heads and cross-linked polyethylene. J. Bone Jt Surg. Am., 1995, 77, 1315-1322.

    Hatton, A., Nevelos, J. E., Nevelos, A. A., Banks, R. E., Fisher, J. and Ingham, E. Alumina-alumina artificial hip joints: a histological analysis and characterisation of wear debris by laser capture microdissection of tissues retrieved at revision. Biomaterials, 2002, 23, 3429-3440. [CrossRef]

    Schmalzried, T. P., Zahiri, C. A. and Woolson, S. T. The significance of stem-cement loosening of grit-blasted femoral components. Orthopedics, 2000, 23, 1157-1164.

    Bader, R., Steinhauser, E., Holzwarth, U., Schmitt, M. and Mittelmeier, W. A novel test method for evaluation of the abrasive wear behaviour of total hip stems at the interface between implant surface and bone cement. Proc. Instn Mech. Engrs, Part H: J. Engineering in Medicine, 2004, 218, 223-230.

    Crowninshield, R. D., Jennings, J. D., Laurent, M. L. and Maloney, W. J. Cemented femoral component surface finish mechanics. Clin. Orthop. Relat. Res., 1998, 355, 90-102.

    Brown, L. T.Use of 3D surface analysis techniques to investigate the wear of matt surface finish femoral stems in total hip replacement. PhD Thesis, University of Huddersfield, Huddersfield, UK, 2006.

    Howell, J. R., Blunt, L. A. and Ling, R. S. M. An analysis of fretting damage seen on explanted femoral stems. J. Bone Jt Surg. Br., 1999, 81 (Suppl. 3), 163. [CrossRef]

    Howell, J. R., Blunt, L. A., Doyle, D., Hooper, R. M., Lee, A. J. C. and Ling, R. S. M.In vivo surface wear mechanisms of femoral components of cemented total hip arthroplasties: the influence of wear mechanism on clinical outcome. J. Arthroplasty, 2004, 19, 88-101.

    Cook, J. E.Fretting wear of total hip replacement femoral stems. PhD Thesis, University of Exeter, Exeter, UK, 1998.

    Ebramzadeh, E., Billi, F., Sangiorgio, S. N., Mattes, S., Schmoelz, W. and Dorr, L. Simulation of fretting wear at orthopaedic implant interfaces. J. Biomech. Engng, 2005, 127, 357-363.

    ISO 7206-4: 2002 Implants for surgery - partial and total hip joint prosthesis - Part 4: determination of endurance properties of stemmed femoral components, 2002 (International Organization for Standardization, Geneva).

    Gruen, T. A., McNeice, G. M. and Amstutz, H. C. ‘Modes of failure’ of cemented stem-type femoral components: a radiographic analysis of loosening. Clin. Orthop. Relat. Res., 1979, 141, 17-27.

    Jasty, M., Maloney, W. J., Bragdon, C. R., O'Connor, D. O., Haire, T. and Harris, W. H. The initiation of failure in cemented femoral components of hip arthroplasties. J. Bone Jt Surg. Br., 1991, 73, 551-558.

    Revell, P. A., AL-Saffar, N. and Kobayashi, A. Biological reaction to debris in relation to joint pros-theses. Proc. Instn Mech. Engrs, Part H: J. Engineering in Medicine, 1997, 211, 187-197.

    Eliades, T., Papadopulos, J. S., Eliades, G., Silikas, N. and Watts, D. C. Multi-technique characterization of retrieved bone cement from revised total hip arthroplasties. J. Mater. Sci.: Mater. Medicine, 2003, 14, 967-972.

    Maloney, W. J., Schmalzried, T. and Harris, W. H. Analysis of long term cemented total hip arthroplasty retrievals. Clin. Orthop. Relat. Res., 2002, 405, 70-78.

    Wang, J., Franzén, H., Jonsson, E. and Lidgren, L. Porosity of bone cement reduced by mixing and collecting under vacuum. Acta Orthop. Scand., 1993, 64, 143-146.

    Bishop, N. E., Ferguson, S. and Tepic, S. Porosity reduction in bone cement at the cement-stem interface. J. Bone Jt Surg. Br., 1996, 78, 349-356.

    Jones, R. E., Willie, B. M., Hayes, H. and Bloebaum, R. D. Analysis of 16 retrieved proximally cemented femoral stems. J. Arthroplasty, 2005, 20, 84-93. [CrossRef]

    Walczak, J., Shahgaldi, F. and Heatley, F.In vivo corrosion of 316L stainless steel hip implants: morphology and elemental compositions of corrosion products. Biomaterials, 1998, 19, 229-237. [CrossRef]

    Meneghini, R. M., Feinberg, J. R. and Capello, W. N. Primary hybrid total hip arthroplasty with a roughened femoral stem: integrity of the stem cement interface. J. Arthroplasty, 2003, 18, 299-307. [CrossRef]

    Sanchez-Sotelo, J., Berry, D. J. and Harmsen, S. Long term results of use of a collared matte finished femoral component fixed with second generation cementing techniques. J. Bone Jt Surg. Am., 2002, 84, 1636-1641.

    Williams, H. D. W., Browne, G., Gie, G. A. and Ling, R. S. M. The Exeter universal cemented femoral component at 8 to 12 years: a study of the first 325 hips. J. Bone Jt Surg. Br., 2002, 84, 324-334. [CrossRef]

    Maher, S. A. and Prendergast, P. J. Discriminating the loosening behaviour of cemented hip prostheses using measurements of migrations and inducible displacement. J. Biomechanics, 2002, 35, 265-275.

    Cristofolini, L., Teutonico, A. S., Monti, L., Cappello, A. and Toni, A. Comparative in vitro study on the long term performance of cemented hip stems: validation of a protocol to discriminate between good and bad designs. J. Biomechanics, 2003, 36, 1603-1615. [CrossRef]

    Liu, C., Green, S. M., Watkins, N. D., Gregg, P. J. and Mccaskie, A. W. Creep behaviour comparison of CMW 1 and Palacos R-40 clinical bone cements. J. Mater. Sci.: Mater. Medicine, 2002, 13, 1021-1028.

    Verdonschot, N. and Huiskes, R. Acrylic cement creeps but does not allow much subsidence of femoral stems. J. Bone Jt Surg. Br., 1997, 79, 665-669. [CrossRef]

    Depositing User: Briony Heyhoe
    Date Deposited: 17 Jun 2008 16:52
    Last Modified: 23 Sep 2014 12:31
    URI: http://eprints.hud.ac.uk/id/eprint/817

    Document Downloads

    Downloader Countries

    More statistics for this item...

    Item control for Repository Staff only:

    View Item

    University of Huddersfield, Queensgate, Huddersfield, HD1 3DH Copyright and Disclaimer All rights reserved ©