The influence of impurities on the growth of helium-induced cavities in silicon

Vishnyakov, Vladimir, Donnelly, S. E. and Carter, G. (2003) The influence of impurities on the growth of helium-induced cavities in silicon. Journal of Applied Physics, 94 (1). p. 238. ISSN 0021-8979

Metadata only available from this repository.

Abstract

The effects of implanted oxygen, carbon, nitrogen, and self-damage on the growth of helium-induced cavities in silicon during high-temperature annealing have been studied. Impurities and helium were implanted into silicon at room temperature. Annealing at temperatures above 1000 K converts small He-filled bubbles into larger empty voids. The mean void size after annealing for 30 min at 1173 K was significantly reduced by the presence of all three implanted impurities. In extreme cases, the mean void radius is reduced from 10 nm, for a pure He implant, to 2.8 nm in a C pre-implanted sample. On the other hand, self-ion damage, unless at or near the level sufficient to cause amorphization, does not significantly affect cavity growth during annealing. We speculate that the presence of impurities significantly reduces the movement of voids by pinning them to dislocations or impurity aggregates or by chemical reactions at the void surfaces.

Item Type: Article
Subjects: Q Science > QC Physics
Schools: School of Computing and Engineering > Electron Microscopy and Materials Analysis
Related URLs:
Depositing User: Graeme Greaves
Date Deposited: 02 Oct 2013 09:29
Last Modified: 09 Oct 2014 10:37
URI: http://eprints.hud.ac.uk/id/eprint/18659

Downloads

Downloads per month over past year

Repository Staff Only: item control page

View Item View Item

University of Huddersfield, Queensgate, Huddersfield, HD1 3DH Copyright and Disclaimer All rights reserved ©