Single Point Diamond Turning of Calcium Fluoride Optics

Luo, Xichun, Sun, Ji Ning, Chang, Wen Long and Ritchie, James M. (2012) Single Point Diamond Turning of Calcium Fluoride Optics. Key Engineering Materials, 516. pp. 408-413. ISSN 1662-9795

Metadata only available from this repository.


This paper aims to develop a cost-effective diamond turning process to obtain nanosmooth CaF2 optics. Diamond tool wear was also carried out through a number of cutting trials. Three CaF2 specimens (diameter of 50 mm and thickness of 5 mm, crystal orientation of (111)) were diamond turned on an ultra precision lathe (Moore Nanotech 350UPL) by a number of facing cuts. In the cutting trials feed rate varied from 1 μm/rev to 10 μm/rev. White spirit mist was used as the coolant. Cutting forces were measured by a dynamometer (Kistler BA9256). Surface roughness of the CaF2 optics and tool flank wear were measured by a white light interferometer (Zygo Newview 5000) and a scanning electron microscope (FEI Quanta 3D FEG), respectively. It was found that using a feed rate of 1 μm/rev surface roughness Ra of 2 nm could be obtained. When the ratio of the normal cutting force to the tangential cutting force was lower than 1 tool wear would initiate. In diamond turning of calcium fluoride abrasive wear was the main tool wear mechanism. Using white spirit mist as thecoolant could avoid generation of thermal type brittle fracture on the machined CaF2 surfaces.

Item Type: Article
Subjects: T Technology > T Technology (General)
T Technology > TJ Mechanical engineering and machinery
Schools: School of Computing and Engineering
School of Computing and Engineering > Centre for Precision Technologies
Related URLs:
Depositing User: Sara Taylor
Date Deposited: 13 Dec 2012 15:13
Last Modified: 13 Dec 2012 15:13


Downloads per month over past year

Repository Staff Only: item control page

View Item View Item

University of Huddersfield, Queensgate, Huddersfield, HD1 3DH Copyright and Disclaimer All rights reserved ©