Liu, Y, Arenas, M, De Frutos, A, De Damborenea, J, Conde, A, Skeldon, P, Thompson, G, Bailey, Paul and Noakes, T. C. Q. (2008) Influence of nitric acid pre-treatment on Al–Cu alloys. Electrochimica Acta, 53 (13). pp. 4454-4460. ISSN 0013-4686Metadata only available from this repository.
The enrichment of copper alloying additions near the surface of sputtering-deposited Al–1.3 at.%Cu, Al–2.7 at.%Cu and Al–30 at.%Cu alloys is investigated following immersion in nitric acid, which is used commercially as a de-smutting pre-treatment. Corrosion of the alloys is revealed at rates in the range 4–13 nm min−1, leading to enrichment of copper in the alloy surface regions. Enrichments are also generated by nitric acid treatment of AA2024-T3 and AA7075-T6 alloys, with levels similar to those achieved by etching in sodium hydroxide solution. Conventional durations of de-smutting treatments in nitric acid have minor influences on the magnitude of enrichment.
|Subjects:||Q Science > Q Science (General)|
Q Science > QD Chemistry
|Schools:||School of Applied Sciences|
|Depositing User:||Sharon Beastall|
|Date Deposited:||10 Jan 2012 09:55|
|Last Modified:||04 Sep 2012 09:49|
Downloads per month over past year
Repository Staff Only: item control page